The color beyond black and white, TeckWrap Black Silver is a marker of class and quality. Present the best of yourself with this stylish wrap.
Specifications
Conformable and reliable Renolit polymeric material. Suitable for complete car wrapping (or any other smooth or curved surface).
The thickness of the film is 0.12mm
The thickness of film with release liner: 0.28mm
Type of film: Pressure-sensitive high-grade polymeric vinyl film with air-release channels
Adhesive: Henkel solvent-based acrylic adhesive, transparent, ultra-weather-resistant, viscosity 1000~3000cps, thickness 12 µm dry
Release liner: Felix Schoeller Release Liner / 20-104-20-1,9 printed, double side PE coated Kraft. One side solventless silicone-coated, air release (ISO 9001, ISO 140001, OHSAS 18001)
Storing period: 3 years if stored in +10°? to +20°? for optimal quality, relative humidity 50%, in original package, away from direct sunlight, in a clean and dry place
Durability/Warranty: Datasheet (Click the link)
Post heating: 65 Celcius
Elongation/Break MD:206.8 / CD:196.4 (Test method: ASTM D882-02)
Tensile Strength: MD:29.5 / CD:24.8 N/mm2 - Speed 200mm/min (Test method: ASTM D882-02)
Dimensional Stability: 2% - Oven/10'*70C(MD) (Test method: ASTM D1204-02)
Surface Tension: 34 dynes/cm (Test method: ASTM D2578-04a, 24 hours after production)
Package: Roll width 152 cm, length 18 m, weight 13 kg
Install tips:
Temperature: from +17°-18°?, usage from -45°? to +45°?
Tools: Standard squeegee with soft (wet) buffer
Conformability: smooth and medium curved surface
Directional: yes
Overlap width: 3-4mm
Important note: The screen's images, colors, and finishes are approximate. For an accurate representation of the product, always check the color swatch. Rolls from the same production LOT number should be used for completing a wrap job, as a slight batch-to-batch variation of color may occur. The film may scratch during the application or a day in and out use. The warranty does not cover the scratching of the film.